Transition from elastic to plastic deformation as asperity contact size is increased
Yong, C. W. Smith, W. Dhir, A. Kendall, K.
Yong, C. W.
Smith, W.
Dhir, A.
Kendall, K.
Authors
Editors
Other contributors
Affiliation
Epub Date
Issue Date
2007-01
Submitted date
Alternative
Abstract
Contacts between a clean sodium chloride pyramidal shaped asperity and a plane NaCl surface have been investigated by molecular dynamics simulations. For small contacts, a few atoms across, the asperity jumped to contact and behaved elastically as normal load was applied. Then, when the force was reversed to detach the asperity, brittle failure occurred without any damage to the crystalline materials. However, as the contact size of the asperity was increased to 6×6 atoms in area, the mechanism of detachment was seen to alter. The jump to contact was elastic and damage free, but the separation could not be achieved elastically, but required plastic deformation, giving extensive energy dissipation and severe damage as edge defects propagated through the asperity. Above this contact size, plastic flow was dominant. However, there is clearly a further transition back to elastic fracture once the asperity becomes large enough for Griffith-type cracking to propagate above 1μm in size, since large sodium chloride contacts are known to be brittle above the micrometre scale, depending on the presence of crack initiating defects. Transition from elastic to plastic deformation as asperity contact size is increased | Request PDF. Available from: https://www.researchgate.net/publication/225130915_Transition_from_elastic_to_plastic_deformation_as_asperity_contact_size_is_increased [accessed Jul 05 2018].
Citation
Transition from elastic to plastic deformation as asperity contact size is increased 2007, 26 (3):235 Tribology Letters
Publisher
Journal
Research Unit
PubMed ID
PubMed Central ID
Embedded videos
Additional Links
Type
Journal article
Language
en
Description
Series/Report no.
ISSN
1023-8883
1573-2711
1573-2711